Abstract
The shape of stiff chains in dilute solution was considered. An average axial ratio was defined to describe the shape of the stiff chains and calculated using Tagami’s model for stiff chains. It was found that the average axial ratio is approximately proportional to λL in the stiff-chain region, where 1/2λ is the persistence length and L is the contour length of the chain. The limiting behavior agrees with Kuhn’s result for a random chain.
Similar content being viewed by others
Article PDF
References
W. Kuhn, Kolloid Z., 68, 2 (1934).
W. Kuhn, J. Polym. Sci., 1, 380 (1946).
C. A. Hollingsworth, J. Chem. Phys., 16, 544 (1948).
C. A. Hollingsworth, J. Chem. Phys., 17, 97 (1949).
K. Šolc and W. H. Stockmayer, J. Chem. Phys., 54, 2759 (1971).
K. Šolc, J. Chem. Phys., 55, 335 (1971).
O. Kratky and G. Porod, Rec. Trav. Chim., 68, 1106 (1949).
R. A. Harris and J. E. Hearst, J. Chem. Phys., 44, 2595 (1966).
N. Saitô, K. Takahashi, and Y. Yunoki, J. Phys. Soc. Jpn., 22, 219 (1967).
Y. Tagami, Macromolecules, 2, 8 (1969).
S. Chandrasekhar, Rev. Mod. Phys., 15, 1 (1943).
N. Saitô and M. Namiki, Prog. Theor. Phys., 16, 71 (1956).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hoshikawa, H., Saitô, N. & Nagayama, K. Average Axial Ratio of Stiff Chains. Polym J 7, 79–85 (1975). https://doi.org/10.1295/polymj.7.79
Issue Date:
DOI: https://doi.org/10.1295/polymj.7.79