Abstract
Linker functionalization is a common route used to affect the electronic and catalytic properties of metal-organic frameworks. By either pre- or post-synthetically installing linkages with differing linker moieties the band gap, workfunction, and exciton lifetimes have been shown to be affected. One overlooked aspect of linker functionalization, however, has been the impact on the metal d-orbital energies to which they are bound. The ligand field differences should result in substantial changes in d-splitting. In this study we use density functional theory (DFT) to study the energetics of d-orbital energy tuning as a function of linker chemistry. We offer a general descriptor, linker pKa, as a tool to predict resultant band energies in metal-organic frameworks (MOFs). Our calculations reveal that simple functionalizations can affect the band energies, of primarily metal d lineage, by up to 2 eV and illustrate the significance of this band modularity using four archetypal MOFs: UiO-66, MIL-125, ZIF-8, and MOF-5. Together, we show that linker functionalization dramatically affects d-energies in MOF clusters and highlight that linker functionalization is a useful route for fine-tuning band edges centered on the metals, rather than linkers themselves.
Similar content being viewed by others
Introduction
MOFs are of increasing interest in catalysis because their molecular level tunability is a feature that has proven useful in photocatalytic applications where careful control of frontier band potentials are required1,2,3. The ability to affect both the band gap and nature of the transition—e.g., metal-to-ligand band parentages—play critical roles in the population and lifetimes of excitons, respectively. There exist several routes to creating and modifying MOF catalysts, including linker functionalization and transmetalation4,5,6. To date, linker functionalization has been largely portrayed to affect the energetics of the linker, and subsequently the linker-based bands in MOFs. The interplay between ligand electronics and metal d-splitting has remained an overlooked and fundamental aspect of MOF chemistry, and the ability to fine-tune-specific bands remains a grand challenge and target for MOF-based catalyst development.
The electronic dependence on composition has been investigated by both theory and experiment, with the aim of developing design principles that can be used to predict material properties pre-synthesis. For example, studies have shown that the electronic structure of the isolated linker is a reasonable predictor for the electronic structure of the MOF5,7,8,9. This result is curious because there are a variety of possible frontier band compositions between MOF structures. The four MOF types are those with, (I) organic valence and conduction bands (e.g., Zr-UiO-6610, Zn-MOF-511), (II) inorganic valence/organic conduction bands (e.g., Zn-NDI12, but these are rare because it is difficult to design a linker that is so readily reduced), (III) inorganic valence/inorganic conduction bands (e.g., Cu-HKUST-113), and (IV) organic valence/inorganic conduction bands (e.g., Ti-MIL-12514). For materials featuring organic valence bands (type I and IV), it is well-established that linker functionalization affects the valence band energy and material ionization potential. For example, the addition of the electron donating group –NH2 reduces the electronic band gap in benzene dicarboxylate (bdc)-containing MOFs by ~1.3 eV4,9. It is decidedly more difficult to affect the valence band energies of systems that have inorganic extrema, simply because there are fewer chemical handles available.
In a 2020 study, Syzantseva and co-workers showed that the free-bdc linker orbitals were good energetic estimates of the MOF-bound linker electron energies7. Hamad and co-workers showed a similar trend for zeolite imidazole frameworks (ZIFs) where the HOMO/LUMO gap of the linker is correlated to the band gap of the resulting MOF5. A combined experimental and computational study by Hemelsoet and co-workers showed that in UiO-66, a MOF whose band edges are primarily linker character, the optical absorption across the HOMO/LUMO of the linker is related to the optical band gap absorption of the MOF15. These electronic structure studies are instrumental in better understanding the photophysical properties of MOFs, but none have thus far taken into account the linker’s effect on the metal d-orbital energies.
Considering the four types of energy alignments, one overlooked aspect of linker functionalization—independent of the MOF frontier band parentage—is the affect that linker functionalization has on d-orbital splitting, i.e., the ligand field effects. Since the d-orbital energies are highly sensitive to changes in ligand field, changes in ligand electron density should influence the stability and energetics of metal d-states. Therefore, linker functionalization should provide a unique avenue to fine-tuning valence band d-orbitals in type II and III MOFs, and conduction band d-orbitals in type III and IV materials.
The application of high-symmetry splitting diagrams are useful predictive tools for transition metal energies, even when the metal coordination environment diverges from the high-symmetry assignments (e.g., the Zn2+ ions in the MOF-5 cluster are locally tetrahedral but are formally C3v, Fig. S1; the Ti4+ centers in MIL-125 are locally octahedral, but are formally C1, Fig. 1a). There are a variety of computational methods one can use to probe the effective ligand field. The most common method involves the calculation of a model octahedral or tetrahedral transition metal complex, and d-splitting is an indicator of relative ligand field strength16,17,18,19,20,21. One can also use charge parsing schemes to assess donor atom charge. The issue with parsing methods is that linker/metal interactions are not limited to σ-donation. For example, Bader charges or other approaches do not directly probe unoccupied orbital contributions (e.g., ligand t2 linker orbitals in tetrahedral systems). Alternatively, the free-linker pKa is a useful descriptor for d-splitting and subsequent band modularity because pKa is a property that depends on the cumulative electronic structure of the Lewis base. Here, we demonstrate that the bands with metal d character can be affected by up to 2 eV depending on linker functionality. We rationalize these energetic perterbations from ligand field theory. Our approach is general and predictive design principle for fine-tuning d-band energies in MOFs and can be used to target valence and conduction band energy manipulation.
Results and discussion
Inevitably, we will show that pKa is a useful predictor of d-orbital energy splitting and hence a valuable approach to fine-tune metal-band energies. However, to understand this relationship we must first discuss the orbitals that should be affected by ligand functionalization. From ligand field theory, a metal in a perfectly tetrahedral or octahedral environment should have their t2 and t2g energy levels (i.e., metal dxy/xz/yz) affected by the π-ligand manifold, respectively. An octahedral splitting diagram with the qualitative inclusion of the ligand π-manifold is shown in Fig. 1b, while a similar tetrahedral splitting diagram can be found in Fig. S1. In octahedral systems, the t2g-to-eg* gap depends on the σ contribution from the ligand, in addition to whether the ligand can π-donate or accept. Since most MOFs are formed with metal-carboxylates, and carboxylates are generally thought to be σ-donors as well as both π-donors and acceptors (since the pz are half-filled), the t2g orbital energy should be elevated with increasing electron density on the carboxylates. However, it is not immediately clear whether the donor or acceptor character is dominant in MOF linkers and will indeed be elucidated with computation. For now, let us assume that carboxylates are weakly π-donating, and functional groups that increase the electron density around the carboxylate should serve to push the t2g orbitals towards the vacuum level. Similarly, the eg energy should be determined primarily by the σ contribution from the ligand, where increased σ density elevates the eg towards the vacuum level.
With this textbook analysis of orbital energies in mind we can now consider the local coordination environments of metals in MOF clusters, Fig. 2. For this study we selected four familiar frameworks, Zr-UiO-66, Zn-MOF-5, Ti-MIL-125, and Zn-ZIF-8. These frameworks allow us to make comparisons between MOFs with the same metal but different ligands, the same ligand with different metals, and different coordination environments. An important aspect in the electronic applications of MOFs is the character of the band edges. MIL-125, a type IV d0 MOF, with a titanium centered conduction band, and each metal center connects to three unique organic ligands. The other three inner-sphere ligating ligands are µ2-OH and bis-µ2-O, Fig. 2a. The other MOFs are type I (ZIF-8, UiO-66, and MOF-5), with linker character at both extrema. UiO-66 also features d0 Zr(IV) with four bdc-carboxylates and two µ3-OH and µ3-O Fig. 2b. Both ZIF-8 and MOF-5 contain d10 Zn(II); MOF-5 features Zn(II) with three bdc-connections, and a single µ4-O (Fig. 2c), while ZIF-8 Zn(II) are ligated by four imidazolates (Fig. 2d). Subsequent linker functionalization should affect the conduction band d-orbitals in UiO-66 and MIL-125, and the valence band in ZIF-8 and MOF-5. The same functionalization will also affect the chemical properties of the free linker itself, such as its pKa and electron energies.
In Pearson’s seminal paper22, he demonstrated that Lewis “hardness”23 could be estimated from the energy of the molecular HOMO and LUMO, aligned to the vacuum level, an example is shown in Fig. S2. Thus, a DFT calculation of functionalized linkers should provide a direct estimate of its hardness, which is related to ligand field. pKa is also dependent on hardness, because the Brønsted acidity of the linker is related to the Lewis basicity of the conjugate base, and the pKa may be calculated through a simple thermodynamic cycle by optimizing the structures of the protonated and deprotonated linker and calculating their energies in the gaseous and (pseudo)solvated phases24.
By plotting the computed electron affinity of the acidic linkers (i.e., LUMO energies for molecules presented in Fig. 3a), and their respective pKa, we find there is a linear relationship between the two, Fig. 3b. Generally, the presence of an electron withdrawing group stabilizes the conjugate base, stabilizing the electron density of the anion. Additionally, the functionality results in a large range of predicted pKa values for functionalized imidazoles (~2–~16 for –NO2 and –CH3 functionalities, respectively), and bdc derivatives (~1.5–4.5, for –F4 and –NH2 functionalities, respectively). These calculations provide the basis for our hypothesis that the linker pKa should be a good descriptor for ligand field strength because it is a property that depends on the ligand electronics.
However, the carboxylate-H+ bond strength (related to the pKa) is in essence a measure σ-density, which formally should not be related to the effect on the band edges in any of these MOFs. This is because the conduction bands in UiO-66/MIL-125 should comprise, among others, the π-donating orbitals on the linker, whereas the MOF-5/ZIF-8 valence bands should comprise the linker’s π-accepting orbitals. Thus, we highlight that the relationship between pKa and predicted band energy in the MOF is a descriptor that conflates several fundamental chemical properties of the linker, and is linearly related to the linker LUMO energy, Fig. 3b.
We sought to monitor the d-orbital energies of the band extrema as a function of linker functionality and relate the band energies to the linker pKa. Critically, to make the comparison the MOF electron energies must be aligned to the vacuum level. This way we can observe the effect of functionalization on metal d-orbital energies relative to one another. Using our code STREUSEL25, we can align the MOF valence band to the vacuum level using a previously described method26. From there, we can plot a density of states, and use the density to direct us to the frontier metal orbitals. For example, Fig. S4 shows the density of states of the ZIF-8 with different linker functionalization. The valence band energy shifts with linker functionalization, and is linker centered at its extrema. The Zn d-states also shift and can be seen moving around slightly deeper in the density of states. Additionally, the band gap of ZIF-8 was calculated to be 5.3 eV, which matches closely with reported values from UV-Visible measurements27. In general, this band gap is reduced as there is more electron withdrawing functionalization on the linker. A similar trend is observed for the other MOFs, Table. S1.
To make a quantitative assessment of the extent to which the metal d-orbitals are affected we follow a general protocol of searching for metal-character bands that we can easily keep track of (e.g., the dxy/xz/yz in Fig. 1a). By selecting a metal-orbital for each system—dxy/xz/yz in all cases—we can then recover their energy and relate it to the free-linker pKa, Fig. 4. There, the plot is divided into two panels; those whose d10 and hence appear in the valence band (MOF-5 and ZIF-8 derivatives) and those that are d0 and appear in the conduction band (MIL-125 and UiO-66 derivatives). Each plot contains limited data points, as there are a limited number of functionalized linkers that are stable in a given structure. As such, the numeric values of gradient serve as more of a qualitative comparison, than a quantitative property. Notably, there is a strong linear relationship between free-linker pKa and d-energy in the MOF, with the most dependence occurring for UiO-66 and MOF-5 (0.49 and 0.38 eV/pKa, respectively). MIL-125 and ZIF-8 are like one another with gradients of 0.16 and 0.13 eV/pKa, respectively. The difference in gradient is to be expected, as each of the MOFs have different coordination environments and these data point to a general observation that metal d-orbitals respond to ligand fields differently in different MOFs (there is not one unified gradient that relates linker functionality to d-energy change).
Given that all slopes are positive, and the orbitals we monitor are dxy/xz/yz in character, we can reinforce the conclusion that less acidic linkers are indeed π-donors as octahedral d0 metals should accept π-electrons and elevate their d-energy in the conduction band, and tetrahedral d10 should see a similar effect but in the valence band. Perhaps more remarkable is the magnitude of band energy shifting. There is a strong linear relationship between pKa and Zr d-energy in UiO-66 and its functionalized derivatives. Unfunctionalized UiO-66 features d-orbitals at –0.75 eV from vacuum, and amination results in elevation of those orbitals to –0.55 eV. This is an interesting result because there is ongoing debate in the literature as to the origin of the Zr(III) ESR signal observed28 upon photo-irradiation of the aminated material, but not the conventional MOF29. We believe that this is because of a more nuanced effect—amination closes the electronic gap from 4.2 to 2.8 eV30,31. Since the d-states are only shifted by 0.25 eV, but the band gap shifted by 1.4 eV, the resulting ligand-to-metal excitation is decreased from 6.2 eV down to 4.5 eV, well within the UV-Vis., Fig. 5a. It is possible that linker functionalization may also affect linker vacancy population, but it is difficult to imagine a vacancy resulting in a significantly stabilized accessible Zr d-state.
In a more subtle case, MIL-125-NH2 shows a 100 meV shift in conduction band energy compared to its unfunctionalized analogue, Fig. 5b. Although 100 meV is relatively small compared to shifts achieved for the other MOFs, it should be detectable from solution phase electrochemical measurements, optical measurements and may even affect the catalytic performance of the MOF for hydrogen evolution32,33,34. Moving from MIL-125-NH2 to MIL-125-F results in a 200 meV shift in conduction band energy. Considering a previous study from our group35, the energy of the conduction band is critical for deliberately disfavoring the hydrogen evolution reaction. Thus, the fluoro-functionalized MOF may be sufficiently stabilizing to turn off hydrogen evolution and increasing H•-atom loading the MOF, Fig. 5b.
In MOF-5, each Zn ion is bound to three bdc linkers and functionalization results in up to 1 eV energy shift of the highest energy Zn dxy/xz/yz orbitals. In the most extreme case, tetrafluoro-bdc pushes the orbital 900 meV deeper into the valence band. Notably, the orbital energy for MOF-5 and its isoreticular pyrene-based analogue, IRMOF-1436, is basically indistinguishable. That is, both Zn ions are deep within the valence bands are redox inactive. This points to a general observation that MOF-5 and isoreticular analogues all feature relatively deep Zn d-states and need to be transmetalated to access redox active metal centers37.
Finally, of the MOFs examined, the ZIF series shows the least goodness-of-fit to a linear regression, while maintaining a strong positive relationship between linker pKa and Zn d-orbital energies. Bracketing the two extremes are methyl-imidazole and nitro-imidazole, with computed pKas of ~16 and ~2, respectively. This vast difference in linker acidity results in dramatic differences of Zn(II) d-energies, from −8.0 to −10.2 eV, or a staggering 2.2 eV in ligand field tuning. The residuals are large because the dichloro-functionalized imidazole is functionalized in the C2,3 position, which is chemically dissimilar to the other functionalizations (per Fig. 3a). In both Zn(II) cases, the orbitals sit within the valence band and are likely not chemically active for photocatalysis. We rather selected them because they highlight the central point of this study—ligand field effects from linker functionalizations can dramatically affect d-orbital energies in MOF clusters.
Together, these data highlight a critical but overlooked aspect of linker chemistry in MOFs: the impact of the linker on the metal d-energies. Of course, synthetic chemists have shown that the linker functionality affects the synthetic conditions in which they are formed, presumably due to differences in acidity of the linker. To account for this difference in acidity, creative solutions to MOF syntheses have been developed38. But even then, little attention has been paid to the effect of metal energetics as the result of differences in acidity. We believe this is an important and fundamental aspect of MOF chemistry, but one that is costly to compute on periodic bulk MOFs. To circumvent this, we showed that there is a positive relationship between linker pKa and d-orbital band energy in four dissimilar MOFs. The same concept will apply beyond type I and IV MOFs examined here and should prove to be a useful design principle in MOF catalyst design. In the most promising examples, we offered one explanation for the observation of Zr(III) d-states in photoexcited UiO-66, and in another example we showed that the conduction band energy of MIL-125 can be tuned by 200 meV using common linker chemistries. More broadly, we demonstrated that linker pKa is a valuable descriptor and predictor of d-orbital energy in MOFs and will vastly accelerate materials discovery for precisely tuned metal energies.
Computational methods
All periodic calculations were performed within the Kohn-Sham DFT framework as implemented in Vienna ab initio Simulation Package (VASP 5.4.4)39. The lattice parameters and ion positions of all MOFs studied were geometrically optimized using the PBEsol functional40, with a 2 × 2 × 2 k-mesh centered at gamma and a 500.00 eV planewave cutoff41. The ionic and electronic convergence criteria were 0.005 eV and 10−5 eV respectively. The electronic structure of the geometrically optimized MOFs were recovered from an HSE06 single point with the same basis at the gamma point42,43. Molecular calculations to determine pKa and LUMO energies were carried out using the Gaussian09 software package44. All free linkers were geometrically optimized using a PBE0 functional, before an HSE06 frequency calculation was performed on the optimized structure. A def2svp basis was used, with tight convergence and a fine density grid. A thermodynamic cycle of solvated deprotonation was used to determine the pKas24, from the sum of thermal and electronic free energy values of the HSE06 calculations. A value of −110.2 kcal/mol was used for the solvation energy of H3O+. Remaining solvation energies were determined through by invoking implicit solvent model.
Data availability
All geometries and output files created for this study are available on FIGshare (https://doi.org/10.6084/m9.figshare.21741365).
References
Wang, J.-L., Wang, C. & Lin, W. Metal–organic frameworks for light harvesting and photocatalysis. ACS Catal. 2, 2630–2640 (2012).
Fu, Y. et al. An amine-functionalized titanium metal-organic framework photocatalyst with visible-light-induced activity for CO2 reduction. Angew. Chem. Int. Ed. 51, 3364–3367 (2012).
Horiuchi, Y. et al. Visible-light-promoted photocatalytic hydrogen production by using an amino-functionalized Ti(IV) metal−organic framework. J. Phys. Chem. C. 116, 20848–20853 (2012).
Li, Y. et al. Effects of ligand functionalization on the photocatalytic properties of titanium-based MOF: A density functional theory study. AIP Adv. 8, 035012 (2018).
Grau‐Crespo, R. et al. Modelling a linker mix‐and‐match approach for controlling the optical excitation gaps and band alignment of zeolitic imidazolate frameworks. Angew. Chem. Int. Ed. 55, 16012–16016 (2016).
Lu, W. et al. Tuning the structure and function of metal–organic frameworks via linker design. Chem. Soc. Rev. 43, 5561–5593 (2014).
Syzgantseva, M. A., Stepanov, N. F. & Syzgantseva, O. A. Band alignment as the method for modifying electronic structure of metal−organic frameworks. ACS Appl. Mater. Interfaces 12, 17611–17619 (2020).
Walsh, A., Butler, K. T. & Hendon, C. H. Chemical principles for electroactive metal–organic frameworks. MRS Bull. 41, 870–876 (2016).
Hendon, C. H. et al. Engineering the optical response of the titanium-MIL-125 metal–organic framework through ligand functionalization. J. Am. Chem. Soc. 135, 10942–10945 (2013).
Winarta, J. et al. A decade of UiO-66 research: a historic review of dynamic structure, synthesis mechanisms, and characterization techniques of an archetypal metal–organic framework. Cryst. Growth Des. 20, 1347–1362 (2020).
Li, H., Eddaoudi, M., O’Keeffe, M. & Yaghi, O. M. Design and synthesis of an exceptionally stable and highly porous metal-organic framework. Nature 402, 276–279 (1999).
Wentz, H. C. et al. Switchable electrical conductivity in a three-dimensional metal–organic framework via reversible ligand n-doping. Chem. Sci. 11, 1342–1346 (2020).
Hendon, C. H. & Walsh, A. Chemical principles underpinning the performance of the metal–organic framework HKUST-1. Chem. Sci. 6, 3674–3683 (2015).
Dan-Hardi, M. et al. A new photoactive crystalline highly porous titanium(IV) dicarboxylate. J. Am. Chem. Soc. 131, 10857–10859 (2009).
Hendrickx, K. et al. Understanding intrinsic light absorption properties of UiO-66 frameworks: a combined theoretical and experimental study. Inorg. Chem. 54, 10701–10710 (2015).
Oliveros R, D. A., Machado, R. A. & Mora, J. R. Quantitative structure–property relationship analysis of the spectrochemical series by employing electronic descriptors from DFT calculations. Mol. Phys. 120, e2040629 (2022).
Shimura, Y. A quantitative scale of the spectrochemical series for the mixed ligand complexes of d 6 metals. Bull. Chem. Soc. Japan 61, 693–698 (1988).
Moens, J., Jaque, P., De Proft, F. & Geerlings, P. A new view on the spectrochemical and nephelauxetic series on the basis of spin-polarized conceptual DFT. ChemPhysChem 10, 847–854 (2009).
Anthon, C., Bendix, J. & Schäffer, C. E. Mimicking the two-dimensional spectrochemical series using density functional computations. Inorg. Chem. 43, 7882–7886 (2004).
Atanasov, M., Ganyushin, D., Sivalingam, K. & Neese, F. in Molecular Electronic Structures of Transition Metal Complexes II (eds. Mingos, D. M. P., Day, P. & Dahl, J. P.) vol. 143, 149–220 (Springer Berlin Heidelberg, 2011).
Singh, S. K., Eng, J., Atanasov, M. & Neese, F. Covalency and chemical bonding in transition metal complexes: an ab initio based ligand field perspective. Coord. Chem. Rev. 344, 2–25 (2017).
Pearson, R. G. Absolute electronegativity and hardness: application to inorganic chemistry. Inorg. Chem. 27, 734–740 (1988).
Pearson, R. G. Hard and soft acids and bases. J. Am. Chem. Soc. 85, 3533–3539 (1963).
Pliego, J. R. Thermodynamic cycles and the calculation of pKa. Chem. Phys. Lett. 367, 145–149 (2003).
Mroz, A. M., Davenport, A. M., Sterling, J., Davis, J. & Hendon, C. H. An electric field-based approach for quantifying effective volumes and radii of chemically affected space. Chem. Sci. 13, 6558–6566 (2022).
Butler, K. T., Hendon, C. H. & Walsh, A. Electronic chemical potentials of porous metal–organic frameworks. J. Am. Chem. Soc. 136, 2703–2706 (2014).
Fabrizio, K., Le, K. N., Andreeva, A. B., Hendon, C. H. & Brozek, C. K. Determining optical band gaps of MOFs. ACS Mater. Lett. 4, 457–463 (2022).
Svane, K. L., Bristow, J. K., Gale, J. D. & Walsh, A. Vacancy defect configurations in the metal–organic framework UiO-66: energetics and electronic structure. J. Mater. Chem. A 6, 8507–8513 (2018).
Sun, D. et al. Studies on photocatalytic CO2 reduction over NH2-UiO-66(Zr) and its derivatives: towards a better understanding of photocatalysis on metal-organic frameworks. Chem. Eur. J. 19, 14279–14285 (2013).
Mancuso, J. L. & Hendon, C. H. Titanium(IV) inclusion as a versatile route to photoactivity in metal–organic frameworks. Adv. Theory Simul. 2, 1900126 (2019).
Nasalevich, M. A. et al. Electronic origins of photocatalytic activity in d0 metal organic frameworks. Sci. Rep. 6, 23676 (2016).
Saouma, C. T. et al. Bulk-to-surface proton-coupled electron transfer reactivity of the metal–organic framework MIL-125. J. Am. Chem. Soc. 140, 16184–16189 (2018).
Fiaz, M. et al. Facile fabrication of highly efficient photoelectrocatalysts MxOy@NH2‐MIL‐125(Ti) for enhanced hydrogen evolution reaction. ChemistrySelect 4, 6996–7002 (2019).
Mohammadnezhad, F. et al. Tuning the optoelectronic properties of hybrid functionalized MIL-125-NH2 for photocatalytic hydrogen evolution. ACS Appl. Mater. Interfaces 13, 5044–5051 (2021).
Mancuso, J. L., Fabrizio, K., Brozek, C. K. & Hendon, C. H. On the limit of proton-coupled electronic doping in a Ti(IV)-containing MOF. Chem. Sci. 12, 11779–11785 (2021).
Eddaoudi, M. et al. Systematic design of pore size and functionality in isoreticular MOFs and their application in methane storage. Science 295, 469–472 (2002).
Brozek, C. K. & Dincă, M. Ti3+-, V2+/3+-, Cr2+/3+-, Mn2+-, and Fe2+-substituted MOF-5 and redox reactivity in Cr- and Fe-MOF-5. J. Am. Chem. Soc. 135, 12886–12891 (2013).
Marshall, C. R., Timmel, E. E., Staudhammer, S. A. & Brozek, C. K. Experimental evidence for a general model of modulated MOF nanoparticle growth. Chem. Sci. 11, 11539–11547 (2020).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Ernzerhof, M. & Perdew, J. P. Generalized gradient approximation to the angle- and system-averaged exchange hole. J. Chem. Phys. 109, 3313–3320 (1998).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Janesko, B. G., Henderson, T. M. & Scuseria, G. E. Screened hybrid density functionals for solid-state chemistry and physics. Phys. Chem. Chem. Phys. 11, 443–454 (2009).
Heyd, J., Scuseria, G. E. & Ernzerhof, M. Erratum: “Hybrid functionals based on a screened Coulomb potential” [J. Chem. Phys. 118, 8207 (2003)]. J. Chem. Phys. 124, 219906 (2006).
Frisch, M. J. et al. Gaussian 09, Revision E.01 (Gaussian, Inc, 2016).
Acknowledgements
This material is based upon work supported by the National Science Foundation under Grant No. [2237345]. C.H.H. acknowledges the support of the Camille and Henry Dreyfus Foundation. Computations were supported by the Extreme Science and Engineering Discovery Environment (XSEDE), which is supported by National Science Foundation Grant ACI-1548562, and the Portland State University machine, Coeus, which is supported by the NSF (DMS1624776).
Author information
Authors and Affiliations
Contributions
C.H.H. and B.G.D. conceived the study. Both B.G.D. and L.I.P. performed DFT calculations. C.H.H. and B.G.D. wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Communications Chemistry thanks the anonymous reviewers for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Diamond, B.G., Payne, L.I. & Hendon, C.H. Ligand field tuning of d-orbital energies in metal-organic framework clusters. Commun Chem 6, 67 (2023). https://doi.org/10.1038/s42004-023-00863-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42004-023-00863-z
This article is cited by
-
Influence of electron cloud density of ligands on the band structure and photocatalytic performance of Zr-MOFs
Journal of Materials Science: Materials in Electronics (2024)
-
Modulation mechanism of electron energy dissipation on superlubricity based on fluorinated 2D ZIFs
Nano Research (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.